Advanced, Monolithic
Zirconia Prosthesis
- Designed to protect dental implants
- Titanium bar reinforced
- Compatible with or without multi unit abutments
- Eliminate debonding issues common with hand cemented ti-bases
- A digitally precise fit protects dental implants
- Bar substructure reduces weight up to 30%
- Aids in shock management up to 15% over no bar
- Ideal aesthetic
- More natural feeling than conventional monolithic zirconia
One Screw Check!
Digital design and computer aided precision milling ensure a fit accurate within <10 microns. Just one more way ZIRTIBAR™ protects implants.
quality
materials
Our zirconia is sourced and formulated for its purity, strength, and lifelike aesthetics, boasting a natural depth and translucency. Reinforced with a titanium bar and you have a perfectly balanced prosthesis that is strong, not overly rigid.

ZIRTIBAR™ zirconia is formulated for optimal aesthetics and strength. Notice the depth and translucency of the zirconia crowns.
titanium
Grade 5
- Surgical grade titanium that is both lightweight and strong with an optimal tensile and yield strength, and high corrosion resistance.
- Full length bar provides even support throughout the arch, whereas individual Ti-bases endure uneven and unequal stress often resulting in debonding issues or implant failure.
Tensile Strength: 860 MPa
Elongation (%): 10
Elastic Modulus: 114-120 GPa
ZIRCONIA
- Tera Harz TC-80DP and Tera Harz TC-80.
- High flexural strength and abrasion resistance.
- Produces durable long-term prostheses.
Flexural Strength: 1200 MPa
Elastic Modulus: 210 GPa
Hardness (HV10): 1250
resin
- Surgical grade titanium that is both lightweight and strong with an optimal tensile and yield strength, and high corrosion resistance.
- Full length bar provides even support throughout the arch, whereas individual Ti-bases endure uneven and unequal stress often resulting in debonding issues or implant failure.
Flexural Modulus: 4500 MPa
Flexural Strength: 160-220 MPa
Shore Hardness (D): 90
Comparison of Printing Materials